High Strength Pourable Epoxy Grout

HIGH STRENGTH POURABLE EPOXY GROUT

Hind ERS 219 is a three component solvent free, free flowing, non-shrinking fast curing epoxy resin system
which can be poured, in/on concrete, steel plate for carrying out structural repair, grouting of heavy foundation
bolt, pocket grouting, padding/heavy duty support for crane, rail and other heavy machineries. The system is
insensitive to water and due to higher density it displaces the water thus making application on damp surface.
The cured resin system possesses high mechanical strength, non-shrinking properties, excellent adhesion, and is
chemical resistant typical of all epoxy resin system. Cracks and voids can be successfully sealed/ bonded with
Hind ERS 219. Though it has high strength, the cured material does not become brittle and remains slight
flexible. Hind ERS 219 is manufactured in pre-measured quantities. Component A- Resin, Component BPolyamide
hardener and Component C- Special Aggregate (Graded Silica flour/sand).
ADVANTAGES
Free flowing and non-shrink system.
Resistance to acids and alkalis.
Moisture insensitive
Useful and helps rapid installation process with high strength.

MIX RATIO
Component A - 2 parts by weight: Component B -1 parts by weight: Component C- 9 parts by weight.
APPLICATION
Preparation of Surface
The area to be treated should be properly cleaned by wire brush or shot blasted.
Mixing
Mix all the Component-B Polyamide Hardener with Component-A Resin. Add Component C Special Aggregate
and again mix well, so as not to entrap air into the product. Mix for 2-3 minutes using a drill and paddle
(maximum 200-350 R.P.M.).Only required quantity of material to be mixed for immediate use. The mixed
material should be kept undisturbed for 2-3 minutes, so that if any entrapped air is there it escapes from the mix.

Cleaning
Clean all tools & equipment immediately after use with, Xylene, Toluene or suitable solvent.

PROPERTIES
Aspect                                                    Comp.A-Liquid, Comp.B -Liquid, Comp.C-Graded Silica
Density                                                   1800 1900 kg/m3
Mix Ratio                                               Comp.A : Comp.B : Comp C = 2:1:9 by weight
Working Time                                       40-45 minutes at 270 C +20 C
Compressive Strength                           Min 30 N/mm2 in 24 hours at 270 C +20 C
75-80 N/mm2 in 7 days at 270 C +20 C
Bond Strength                                      1.5-2 N/mm2 in 7 days at 270 C +20 C
Tensile Strength                                   12.5-14 N/mm2 in 7 days at 270 C +20 C
Flexural Strength                                 20-25 N/mm2 in 7 days at 270 C +20 C
Chemical Resistance                            Is not affected by wide range of chemicals, oils etc.
Shrinkage                                             Non-shrink

SHELF LIFE
12 months from the date of manufacture in unopened condition and stored in a cool place under shade.

PACKING
12 & 18, Kg. Kit or as required.

HANDLING PRECAUTION
Hind ERS 219 212 is non-toxic but ingestion is to be avoided. Any splashes to the skin must be washed with
water. If contact with eyes occurs, wash well immediately with water and seek medical advice.