Epoxy Zinc Rich Primer - 24 Kg/tin, Smooth Film With Hb Pencil Hardness, Anticorrosion Protection For Steel Structures, 75 µM Dry Film Thickness

We are dealing in market as major manufacturer and exporter of TH 01 Epoxy Zinc Rich Primer in Wuhan, Hubei, China.

Main functions:
It is widely used in metallurgy, containers, all kinds of transportation vehicles, shot blasting of steel plate pretreatment in engineering machinery, particularly suitable for steel structure anticorrosion, which is the ideal primer of metal pretreatment shot blasting and anticorrosion maintenance.
Technical indicators paint film appearance : the paint film is smooth and the colors conform to standard samples
drying time: standard single-coating thickness, 25 a ,
dry to toucha 2 h, hard drya 12h pencil hardness:a YHB
adhesion:a 2 (adhesion teat by scratch, grade)
Impact strength:50 kga c cm, bending test:a 1mm
Welding burn width:a 15mm
Resistance to salt water (3%, 168 hours), no bubbles, no shedding, no rust
Packaging specifications Paint:24 kg/tin, curing agent:2.4 kg/tin.
Ratio of basic parameters: paint: curing agent = 10:1 (weight ratio)
Construction time:4hi i 25a i
spreading rate in theory: thickness of dry film 75 um 3.13 a / kg
Volume solids: 59%
Specific gravity:2.52kg/L
recommended coating procedures used as precoating primer, 10 I m of coating, 25A 5I m
Used as anticorrosive premier, the thickness of dry film 75A 5I m
This product is used together with micaceous iron oxide epoxy antirust intermediate paint