Orange And Yellow Th 04 Epoxy Micaceous Iron Oxide Intermediate Paint

We are highly proficient manufacturer and exporter of TH 04 Epoxy Micaceous Iron Oxide Intermediate Paint in Wuhan, Hubei, China.

Specifications:
Appearance of paint film: Rust, or gray, smooth paint film;
drying time: Standard single-coating thickness, 25 a ,
dry to toucha 2 hours, hard drya 24 hours, pencil hardness:a Y HB, adhesion:a 2 (adhesion teat by scratch, grade)
Impact strength:30 kga c cm, bending test:a 1mm
Resistance to salt water (3% NaCl solution) 168 H:No bubbles, no rust
Packaging specifications Paint: 22 kg/barrel, curing agent: 4.4 kg/tin.
Ratio of basic parameters: Paint: curing agent = 5:1 (weight ratio)
Construction time:4hi i 25a i
spreading rate in theory: Dry film thickness 125 um 3.05 a / kg
Volume solids:80%
Specific gravity:2.1kg/L
matching paint (former working procedure) TH - 01 epoxy zinc-rich primer
(latter working procedure) HL - 358 all kinds of polyurethane paint,
Surface treatment The binder shall be clean and free from all contaminants such as oil and dust, and conduct treatment of abrasive blasting or shot blasting, reach Sa2.5 level in Sweden, and the manual mechanical rust removal shall reach St2 - 3 level.
Coating method Airless spraying: Dilute agent: X - 7 special diluent
dilution rate0 ~ 25% (calculated by paint weight)
Inner diameter of nozzle: About 0.4 ~ 0.5 mm
Spraying pressure:15i 20Mpa
Air spraying: Dilute agent: X - 7 special diluent
dilution rate30 ~ 50% (calculated by paint weight)