Ladle Lining Alumina Length: 3-5 Millimeter (Mm)

Ladle Lining Alumina    ( ADLAD-AL)

We are offering a wide assortment of Ladle Lining Material (ADLAD-AL) that is made available in several quantities as per requirement. The offered product is specially used for lining the ladles used in foundries for transferring the molten metal from furnace. Our ingenious professionals formulate this product with the use of supreme quality silica, quartz and other ceramic binders by employing sophisticated methods. Tested on defined parameters of quality, this Ladle Lining Materials can be availed at industry leading rates.  

Features:

• Easy to apply
• Safe to use
• Longer shelf life
• Precise composition

Preparation of Mixtures

• Supplied in dry form using air-tight bags
• Material should be unpacked on clean surface for further usage
• Mix well before addition of water
• After mixing required amount of water should be added that is around 6-8% depending on the consistency required
• Minimum amount of water should be added so that lining does not crack while preheating
• After water addition, it should mix again thoroughly
• For the development of full plasticity, mixture should be covered with wet gunny bags for 8 to 12 hours

Important Note:

• One should take care of removal of strings while unpacking material from bags so that it will not mix with material.
• Remove this kind of material which will burn, as this will create cavity on heating
• Hot metal will enter such cavity and will damage lining resulting in reduction of lining life.

Method of Applications

• Put small handballs made of the mixture in ladle to be lined.
• Surface should be prepared of required thickness (Thickness will depend on capacity of the ladle varying from 2 to 6 or more).
• For proper compressing of the applied material, surface should be rammed with wooden hammer
• It is advised for bigger size ladle there should be a steel former prepared with complete ramming while applying material.
• It should be perfectly dried so that extra water evaporates.
• Dried ladle should be preheated with wood fire before using the same.

Technical Specifications

• AI2O3:50-55% Min.
• SiO2: 40-45% Min.
• Grain size: 0 to 4mm
• Packing: 50kg bag.