Hiperco 50 - Cobalt-iron-vanadium Soft Magnetic Alloy 0.05mm To 1.51mm Thick, 47.5-49.5% Cobalt Content - Highest Saturation Induction 2.4t, High Curie Point 940c, Exceptional Thermal Stability

COBALT-IRON SOFT MAGNETIC ALLOY HIPERCO 50

HIPERCO 50 is a high saturation magnetic induction strength iron cobalt vanadium soft magnetic alloy. In the existing soft magnetic materials, the alloy has the highest saturation magnetic induction 2.4T and a high Curie point 940 C. Due to the high saturation magnetic induction, when manufacturing a motor of the same power, the volume can be greatly reduced, and the weight can be reduced, which is less than 50 Percent of that of an ordinary motor. Moreover, the motor has high sensitivity, low heat generation, good stability and long life. Due to the high Curie point, the alloy can be operated at higher temperatures where other soft magnetic alloy materials have been completely demagnetized and maintain good magnetic stability. The performance stability of the motor is better than that of the permanent magnet motor at higher operating temperatures.

The alloy is melted using Vacuum Induction Melting VIM techniques.

SPECIFICATIONS: ASTM A801-14 Alloy 1, DIN EN 60404-8-6 F11

CHEMICAL COMPOSITION

C 0.01 , Mn 0.15 , Si 0.15, P 0.015 S 0.01 , Ni 0.25 , Cr 0.10 ,Co 47.5-49.5 , V 1.75-2.10 , Fe Bal.

TYPICAL VALUES OF DC-MAGNETIC PROPERTIES After Magnetic final annealed

Induction (B) at 1600A/m 2.271T
Induction (B) at 4000A/m 2.354T
Induction (B) at 8000A/m 2.389T
Coercive force ,Hc 45.58A/m
Notes:
Typical values measured on wound cores strip material 0.0138 in/0.35mm after annealing treatment at 870 C in dry pure hydrogen

FEATURES:

Highest Saturation magnetic induction
Higher curie temperature
High magnetic flux densities
High magnetostrictive coefficient
C. maximum permeability
Low D.C. coercive force and low A.C. core loss

FURTHER PROCESSING (Heat Treatment)

A final heat treatment (magnetic final annealing) is mandatory for achieving the magnetic and mechanical properties. The necessary growth of the grains in the material, and hence the accompanying improvement in the characteristic magnetic values, only occurs during the final annealing.

The maximum magnetic properties of HIPERCO 50 are best achieved by annealing for 5 hours at 865 C to 875 C in a pure dry hydrogen atmosphere (-40 C dew point). Cooling in the blow 870 C to 750C range at 50C per hour and 750C to 300C at 200C per hour is recommended. In order to retain the maximum properties this anneal should be done after all manufacturing of the part is completed.

XAGY does not sell HIPERCO 50 products in the (magnetic) annealed condition.but we are provide the option of heat-treatment processing techniques and Recommendations!


APPLICATION- Rotor and Stator laminations in motors and generators

FORMS OF SUPPLY

STRIP Thickness 0.05MM to 1.51MM
PLATE Thickness 1.52MM to 3.0MM
ROD Diameter 20MM to 500MM