Hz-ag1p 1% Low Silver Copper Phosphorus Brazing Alloy Welding Filler Metal Rods Dimensions: 2.0*500 Millimeter (Mm)

Having an exceptional information in this industry, we are involved in Manufacturing, Exporting and Supplying an exceptional quality variety of HZ-Ag1P 1% Low Silver Copper Phosphorus Brazing Alloy Welding Filler Metal Rods to our clients by being centered in China, Nuevo Leon, Mexico.

COMPOSITION:
Silver 1.00 wt%
Phosphorus 6.00 wt%
Copper Balance
Tin 0.15 wt% max
Total Other Elements 0.15 wt% max.

MATERIAL PROPERTIES:
Solidus 1190oF (643A A C)
Liquidus 1510oF (821A A C)
Brazing Range 1450-1600oF (788-871A A C)
Specific Gravity 8.085
Density (toz/cu in) 4.261
Color Light Copper

DESCRIPTION:
HUAZHONG HZ-Ag1P is extremely fluid at brazing temperatures and will penetrate joint with very littleclearance. Melting of HZ-Ag1Pis virtually complete at 788A A C.Best results areobtained when brazing slightly above Liquidus temperature with clearances of .001-.003". Thephosphorous content of HZ-Ag1Pacts as a fluxing agent and no flux is necessary whenbrazing copper to copper joints.However, when used with other compatible metals, a brazing flux must be used to promote wetting, bonding, and flow throughout the joint.

APPLICATIONS:
It is used for the brazing of copper and copper alloys, brass and bronze. It is primarily used for the joining of copper-to-copper on vibration free joints. It is very effective for joining tight fitting copper pipe and tubing. It should not be used on ferrous metalsor alloys containing more than 10% nickel due to the formation of brittle intermetallic phosphide compounds.

AVAILABLE FORMS:
Standard forms of HZ-Ag1P are wire,flat wire, ring, strip, rod.