C15000 Zirconium Copper Strip - 0.1~2.0 Mm Thickness, Bright Color | High Electrical Conductivity, Solution Treatable Alloy, Mill Finish

We are a prominent Exporter, Manufacturer, Distributor & Supplier of C15000 Zirconium Copper Strip based in Shanghai, China.

CuZr UNS.C15000Zirconium Copper is an excellent and unique copper alloy with high electrical conductivity, hardness, and ductility, moderate strength, and excellent resistance to softening at elevated temperatures. The addition of 0.15% zirconium (Zr) to copper results in a heat treatable copper alloy which may be solution treated and subsequently aged to produce these desirable properties. Rod is supplied from the mill in the fully aged and drawn condition so no further heat treatment is required by the fabricator. The softening temperature of properly heat treated C15000 rod exceeds 500A C as compared to unalloyed, pure copper which softens at 200A C and silver bearing coppers which soften at 350A C.

Chemical Composition:
Zr: 0.10-0.20%
Cu+Ag: min.99.8%
Note:Copper plus additions equal 99.90% minimum.

Typical Physical Properties:
Density at 68A F: 0.321 Lbs./In.3
Specific Gravity: 8.89
Melting Point (Liquidus):1080A C (1976A F)
(Solidus):980A C (1796A F)
Coefficient of Thermal Expansion per A F:9.4 x 10-6 (68-212A F)
9.8 x 10-6 (68-572A F)
11.2 x 10-6 (68-1200A F)
Electrical Conductivity at 68A F (volumetric): 85-95% IACS (aged and drawn)
55-72% IACS (solution annealed)
Thermal Conductivity Btu/ft.2/ft./hr./A F at 68A F: 212
Modulus of Elasticity - Tension:18,700 ksi
Note:
1). the units are based upon US Customary.
2). the typical physical properties apply to age hardened products.
International Specification:
Rods/Bars/Plates/Sheets:UNS.C15000, RWMA Class 1, SAE J461,463; ISO5182-1991
European Standards:CuZr, DIN 2.1580, CW120C to EN