316l Stainless Steel Plate - 0.03% C Max C, 12.0-15.0% Ni, 16.0-18.0% Cr, 2.0-3.0% Mo | Exceptional Corrosion Resistance, High Temperature Strength, Lustrous Finish, Softening Point 1375-1450°c, No Magnetic Properties

These 316L Stainless Steel Plates appearance luster, nice, we have added mo in producing, so it is excellent in Corrosion resistance especially in resistance to some corrosion resistance
main chemical constitution:% Ca 0.03i Sia 1.00i Mna 2.00i Pa 0.035i Sa 0.03 i Ni:12.0-15.0i Cr:16.0-18.0i Mo:2.0-3.0i
Stainless steel plate heat treatment state: softening point 1375~14500C.
Solution treatment: 1010~11500C.
Working condition: Annealing solid solution state NO.1i 2Bi N0.4,HL Surface state.
Mechanical properties: tensile strength (mpa)620 MIN, yield strength(mpa)310min, elongationi %i 30min, Area reduction(%)40min. For added Mo, so the corrosion resistance of atmospheric corrosion resistance and high temperature strength are very good, it can be used in hard condition. Processing scalloping optimal (no magnetic); excellent high temperature strength, Solid solution state without magnetic, cold rolled products have exterior luster.