Rutile Titanium Dioxide - R2 Grade, 90% Tio2 Content, Surface Treated With Silicon And Aluminum | High Whiteness, Low Oil Absorption, Excellent Dispersion In Alkyd Systems

Basic Characters of Rutile Titanium Dioxide :
ProcessRutile paint produced by sulfate process
Surface treatmentTreat with Silicon ,Aluminum, ,special organic substance covering
Standard Classificationi ISO 591-1i : R2
Specific gravity (ISO 787-10) :3 .9g/ cm3
TiO2 content(ISO 591-1) : a Y90%
105a volatile under packagei ISO 787-2i : a 0.5%
Soluble substancesi ISO 787-2i : a 0.5%
Residue on sievei 45I mi (ISO787-18) : a 0.05%
Rutile transformation Rate : a Y97%


Application Conditions:
Whiteness of oil Systemi L*i Note.1 94.5-95 Hue(b*) Note.11.7-2.3
Relative Scattering Strengthi ISO 787-24i Close to the samplei 95-105i %
Color within the color Systemi ISO 787-25i Close to the sample color a Ea 0.3
PH Value of aqueous suspension i ISO 787-9, 7.0-8.5
Oil Absorption Volumei ISO 787-5i a 20g/100g
Resistivity of aqueous extracti ISO 787-14i a Y50ICa cM
Dispersion under high-speed mixing of Alkyd system Note.2a 25I m

Test instructions:
1.Test for whiteness of oil system(L*) and Hue(b*):Grind the Titanium dioxide with grinding mill, to make a film with thickness of 100I m. Calibrate with ASTM standard ceramic tile by Differential Colorimeter. Then test the surface of the film and indicate with CIE L*,a*,b*.
2.Test for Dispersion under high-speed mixing of Alkyd system: In the alkyd resin system, test with Scraper fineness gage after dispersion by high-speed mixer. Other items please refer to ISO standard.