Hot Dipped Galvanized Wire - Low Carbon Steel, 3.8mm To 0.19mm Diameter, 45 To 300 Microns Zinc Coating Thickness, Exceptional Corrosion Resistance And Durability

Salient features of Hot Dipped Galvanized Wire :
1.Production process: Low carbon steel wire rod, after drawing molding, pickling, annealing, hot galvanized. Cooling system.
2.Galvanized wire characteristics: galvanized iron wire has good toughness and elasticity, the highest on the zinc content can reach 300 grams / square meter. Has galvanized layer thickness, corrosion resistance.
Hot dip galvanizing is heated in the melting zinc liquid dip coating, production speed, coating thickness but not uniform, to allow the market to a minimum thickness of 45 microns, up to a maximum of 300 microns above. The darker color, consumption of zinc metal, and the metal substrate is formed into layers, good corrosion resistance, the outdoor environment can be maintained for decades of hot dip galvanizing
because the coating thicker than galvanized, hot galvanized have better protection performance, so it is to be used in harsh working environment protection coating on steel parts. Hot galvanized products in chemical equipment, oil processing, marine exploration, metal structure, electricity, shipbuilding and other industries are widely used in agricultural fields, such as pesticide spray irrigation, greenhouse as well as the construction industry such as water and gas transportation, wire casing, scaffolding, bridge, highway guard rails and other aspects, in recent years has a lot to be used.
3 Sizes of hot-dipped galvanized wire: 8# to 36#(wire diameter ranging from 3.8mm to 0.19mm)