Pigmented Pu Coating

High performance Acrylic Poly-ol based ,Aromatic isocyanide cured P.U Clear, intended for use as top coat transparent coating with excellent chemical and water resistance.

Recommended use :-This product is intended for use as a top coat for base coat and direct on wood to provide excellent hardness & chemical resistance coating. It is recommended as Topcoat for providing better durability, excellent gloss and colour retention , good stain and chemical resistance along with good hardness and flexibility .

• Acceptable for use in OEM and General Industry.
• Excellent chemical & water resistance .
• Temperature resistance up to 80C.
• Drying: Air dry / Forced drying: 80C / 30 min.

• Property Value
• Colour: Water white clear
• Supply viscosity with B-4 Cup @30 ^oC: 60+5 sec
• % Solid Content: 46 + 2
• Specific Gravity: 0.98 + 0.03
• Mix Ratio by Volume: 4 : 1
• Pot Life: >3 hrs @30C
• %Thinner intake: 35 - 40 %
• Coverage: 12-14 sq.m / litre @ 30-35 microns (Theoretical)
• Curing Time: @ 80 deg C for 30 min.
• Shelf Life @ 30 C: 1 year.
• Recoat Time: 24 hrs or after forced drying.
• Temperature Resistance: 80 deg C
• Gloss: > 90 units at 60C
• Flexibility: Good
• Chemical resistance: Good
• Cured Hardness (Pencil): 2H

Surface Preparation : The surface should be clean, dry and free from oil, grease, dirt,& other foreign contamination. The surface should be assessed and treated in accordance with ISO 8504.

• Mix Part-A & Part B in recommended ratio in clean container and mix for 2-3 min.
• Dilute above solution with Compatible Thinner. Set application viscosity 18-22sec.
• Filter with fine filter cloth (600 mesh size)
• Ensure the surface is free from foreign contaminations.
• Set air pressure at 40-50 psi
• Spray to obtain a DFT of 30- 35 microns
• Air dry / force dry in dust free zone.

Storage : Store containers in a dry, cool, well ventilated space and away from source of heat and fire.Loose containers must be kept tightly closed.