Ceramic Fiber Fire Proof Rope - Ceramic Fiber Yarn Braided, Fiberglass/sus304 Reinforced, 1050â°c Max Temp, Acid And Metal Erosion Resistant

Ceramic Fiber Twisted Ropes

Product Description

Ceramic fiber twisted ropes use aluminosilicate ceramic fiber as the main raw material and are manufactured through spinning and weaving processes. According to use temperature and working conditions, fiberglass or heat-resistant alloy wire can be added as reinforcement material. Fiberglass-reinforced models have a continuous use temperature of 650C; metal wire-reinforced models have a continuous use temperature of 1000C. The product has a short-term tolerance temperature up to 1260C.

The product can resist splash erosion from molten metals such as aluminum and zinc.

Product Parameters

Item Value

Color White

Short-term tolerance temperature 1260C

Fiber diameter 3~5m

Aluminum oxide (AlO) 45~48%

Silicon dioxide (SiO) 45~55%

Iron(III) oxide (FeO) 0.7~1.2%

Calcium oxide, sodium chloride (CaO&NaCl) 0.43%

Moisture content <2%

Organic fiber content <15%

Note: The above chemical composition is the composition of the ceramic fiber base material.

Product Specifications

Ceramic Fiber Twisted Rope

Item Working Temperature (C) Diameter (mm)

Fiberglass reinforced 650 3,4,5,6,8,10,12,14,15,16,18,20,25,30,35,40,50

Metal wire reinforced 1000

Ceramic Fiber Three-Strand Twisted Rope

Item Working Temperature (C) Diameter (mm)

Fiberglass reinforced 650 6,10,14,16,20,22,25,30,40,50

Metal wire reinforced 1000

Ceramic Fiber Three-Strand Felted Twisted Rope

Item Working Temperature (C) Diameter (mm)

Fiberglass reinforced 650 6,9,13,16,20,22,25,32,38,40,50

Application Scope

Suitable for thermal insulation of kilns, high-temperature pipelines, and vessels; sealing of furnace doors, valves, and flanges; production of high-temperature furnace door curtains; thermal insulation protection for engines and instruments; fire-resistant cable wrapping and high-temperature equipment thermal insulation wrapping; flue lining protection.

Working Condition Suitability and Restrictions

Different reinforcement materials of this product correspond to different use temperatures. 1260C is only the short-term tolerance temperature; long-term over-temperature operation is prohibited. The product can only withstand short-term splashing of molten aluminum and zinc, and cannot withstand continuous erosion or immersion by molten metal.

The product is suitable for dry static thermal insulation, sealing, and protection conditions. It is not suitable for conditions involving strong acid or alkali corrosion, long-term liquid immersion, high-speed medium erosion, high-frequency severe friction, or continuous open flame burning. The product is only a thermal insulation wrapping auxiliary material and has no independent fire-resistant or fireproof structural qualification.

Usage Precautions

Cutting, processing, and installation of ceramic fiber material generate fiber dust. Maintain ventilation during operation, wear dust-proof protective equipment, and dispose of waste in accordance with local environmental regulations.

The product contains a small amount of organic fiber. Initial high-temperature use may produce carbonization and smoking, which is a normal process characteristic and does not affect product performance.

Use temperature should be matched according to reinforcement material. Over-temperature and over-working-condition use are strictly prohibited.

During use, regularly inspect product condition. In case of powdering, damage, shrinkage, or failure, replace promptly.

All technical data are for reference only. Actual performance depends on usage conditions. Users should conduct their own suitability testing and comply with relevant safety regulations and standards.