Antifoaming Agent T602 - White Micronized Powder, 135-150â°c Melting Point, Low Volatile Content, Excellent Compatibility And Air Release Properties

Chemical A Additives, coating additives, Antifoaming agent ,T602
Antifoaming agent T602
I. Basic performance and application
T602 antifoaming agent can eliminate the air hole and pinhole from coating film during spray coating construction because the iron casting and aluminum casting has inadequate density and water content. During powder melting, it can improve the air release of coat. It can reduce the use of benzoin relatively and has good compatibility with other materials.
II. Technical indexes
Appearance: white micronized powder
Melting point: 135~150centidegree
Volatile content: Less than or equal to0.2%
III. Basic ingredients of powder coating (full gloss, white powder) (dose: 0.5% inner extruding)
NameWeight
Epoxy resin (E-12)300
Polyester resin (5: 5)300
Titanium pigment (rutile)200
Precipitated barium sulfate170
T88 pure leveling agent10
T701 luster-enhancing agent 10
T602 antifoaming agent5
T312 high light wax5
IV. Coating manufacturing technology:
Extruder: double screw extruder
Extruder prezone temperature: 105 degree
Extruder postzone temperature: 120 degree
Extruder speed: 30HZ
V.Attention:
The trial should be carried out before mass production. After inspection and confirmation, the production will be started. Please firmly seal the product and keep it away from fire. Store in shady and dry place.
The product doesnot contain heavy metals in compliance with European ROHS standards.