Saturated Polyester Resin - PET Grafted Thermosetting Material, Smooth Texture, Black Color, Optimal Surface Finish
MOQ1a" Paint/Paints
Surface FinishSmooth
TextureSmooth
Physical Forma>oa1/2"
Raw MaterialPETaEURPTA
Applicationc2%0aeoe<<aeP,ae-tmeC/+aYY
ColorBlack
Dezhou Longtian Environmental And Technology
Dezhou
Economic Saturated Polyester Resin 562 Hydroxyl 2.0 Blue Steel, Weather Resistant, High Hardness, Good Adhesion, Coil Primer
ColorBlue
MaterialSteel
PackagingDrums
Hydroxyl2.0
ApplicationCoating
FeaturesHigh performance, Weather resistance, Good adhesion, High hardness, Gloss retention, Cost effective, Coil primer
Saturated Polyester Resin for Powder Coating P1601-2
Acid value50~56 mgKOH/g
Viscosity3000~6000 mPa.s
Gardner ColorMax.3
Softening point95-100°C
Glass transition tempapprox.54°C
Film thicknessApprox.60μm
Saturated Polyester Resin - High-Quality, Affordable Pricing | Ideal for Various Applications
MaterialPolyester resin
ViscosityVariable
Density1.1-1.3 g/cm³
Shelf life12 months
PackagingDrums
ApplicationMolding
Saturated Carboxyl Polyester Resin TM5180 - White, Solid, 1.2 g/cm³, 1000cps Viscosity | Flatting, Film Chubbiness, Storage Stability, Mechanical Strength
ColorWhite
FormSolid
PackagingBottles
SolubilitySolvent
Density1.2 g/cm³
Viscosity1000cps
Zhejiang Tiansong New Materials Co., Ltd
Hangzhou
BK-5001 Thermosetting Acrylic Resin
Molecular weightAround 1000
Solids contentApproximately 3000
AppearanceClear liquid
PackagingBottles
ApplicationCoating
CrosslinkingReactive
Saturated Polyester Resin for Powder Coating P1501-2
AppearancePale granules
Acid value65~75 mgKOH/g
Viscosity7000~11000 mPa.s
Softening point95-100â
Glass transition tempapprox.54â
Film thicknessApprox.60 m
Saturated Polyester Resin For Powder Coating
Acid value50~56 mgKOH/g
Viscosity3000~6000 mPa.s
Softening point95-100
Glass transitionapprox.54 C
Curing cycles20min at 180
Product typePolyester resin
All Color Unsaturated Polyester Resin
Viscosity1000-5000cps
Density1.1-1.3 g/cm³
Gel time10-30 min
Cure time24-48hrs
Packaging20kg drums
StorageCool and dry place
Amino Resins - High-Quality Synthetic Polymer | Versatile Applications, Affordable Pricing
Product TypeChemical Resin
FormLiquid
ColorYellow
ViscosityVariable
Solid Content60-70%
UsageCoating, binding, and adhesive applications in various industries.
Acrylic Resins - Premium Quality, Versatile Application, Excellent Durability, Affordable Pricing
Product TypePolymer Resin
ColorClear
FormLiquid
ViscosityVariable
AppearanceTransparent
UsageCoatings, adhesives, and casting
Epoxy Resin - Superior Grade Material | High Quality, Nationally Appreciated
Chemical TypeEpoxy
ViscosityMedium
Pot Life24 hours
Cure Time24 hours
ColorClear
PackagingVarious
FAQs Related to Saturated Polyester Resins In Dezhou
How many saturated polyester resins products are available in Dezhou?
Where can I find saturated polyester resins nearby Dezhou?
Can I trust the Dezhou Based Saturated Polyester Resins suppliers listed on Tradeindia?
How many Dezhou based Saturated Polyester Resins manufacturers are there?
What is the delivery time for saturated polyester resins in Dezhou?
Polyester Resin - CE3058 95/5 Pure Saturated Carboxyl | Excellent Leveling, Storage Stability, Yellowing Resistance, High Gloss Finish
AppearanceGranular
Viscosity1000-2000 mPa.s
Softening point100.0-115.0 °C
Acid Value28.0-34.0 mgKOH/g
Glass Transition Temp54.0-58.0 °C
Packaging25kg PE bag
Saturated Carboxyl Polyester Resin
AppearanceOff-white
Viscosity1000-1800 mPa.s
Softening point100-110 °C
Acid Value20-26 mgKOH/g
Glass Transition Temp52-58 °C
Cure Condition10min/200°C
Pure Polyester Resin
AppearanceGranular
Viscosity1000-3000 mPa.s
Softening point105.0-125.0 °C
Acid Value28.0-38.0 mgKOH/g
Glass transition tempApp.62.0 °C
Packaging25kg PE bag
Durable Polyester Resin
Viscosity2000-3500 mPa.s
Softening point105.0-120.0 °C
Acid Value30.0-36.0 mgKOH/g
Glass Transition TempApp.60.0-64.0 °C
AppearanceLight granule
Packaging25kg PE bag
Hybrid Polyester Resin
AppearanceGranular
Viscosity200 mPa.s)
Softening point95.0-115.0
Acid Value32.0-40.0 mgKOH/g
Glass Transition TempApp.55.0
Packaging25kg
Hybrid Polyester Resin TS6700
AppearanceGranular
Viscosity1000-1800 mPa.s
Softening point95.0-115.0 °C
Acid Value52.0-58.0 mgKOH/g
Glass Transition Temp>53.0 °C
Resin typePolyester
Pure Polyester Resin TGIC
MaterialPolyester resin
TGIC7%
TiO240%
BaSO4200%
Flow Agent10%
GLP70110%
Pure Polyester Resin CE2098B
AppearanceOff-white
Viscosity1000-3000 mPa.s
Softening point105.0-125.0 °C
Acid Value28.0-38.0 mgKOH/g
Glass Transition TempApp.62.0 °C
Chemical CompositionPolyester Resin
Hybrid Polyester Resin KM6090 - Polyester Resin 60:40 Epoxy Mix, Light Yellow, Viscosity 200-2000 mPa.s | Excellent Leveling, High Transparency, Storage Stability, Anti-Interference
AppearanceLight yellow
Viscosity200-2000 mPa.s
Softening point95-115 °C
Acid Value49-58 mgKOH/g
Glass Transition Temp55°C
Mixing ratio60:40
Pure Polyester Resin CE2098
AppearanceGranule
Viscosity200 mPa.s
Softening point105.0-125.0
Acid Value28.0-38.0 mgKOH/g
Glass Transition TempApp.62.0
Mixing ratio93/7
50:50 Hybrid Polyester Resin
AppearanceOff-white
Viscosity500-2000 mPa.s
Softening point95.0-115.0 °C
Acid Value70.0-82.0 mgKOH/g
Glass TransitionApp.56.0 °C
TypeHybrid Polyester
Hybrid Polyester Resin 70:30
AppearanceLight yellow
Viscosity1500-2500 mPa.s
Softening point100.0-115.0
Acid Value26.0-32.0 mgKOH/g
Glass TransitionApp.52-58.0
Curing Condition180/18Min or 200/10Min
Pure Polyester Resin 90:10
AppearanceLight yellow granule
Viscosity1000-2000 mPa.s
Softening point100.0-120.0
Acid Value50.0-56.0 mgKOH/g
Glass Transition TempApp.61.0-65.0
Cure Condition15min/200
HAA Cure Pure Polyester Resin
AppearanceGranule
Viscosity200 mPa.s
Softening point105-120
Acid Value28-34 mgKOH/g
Glass Transition Temp58-62
TypePolyester resin
Carboxyl Saturated Polyester Resin Tp4060
MaterialPolyester resin
ColorOff-white
Purity99%
Viscosity1000-2000 cps
Density1.2 g/cm³
Melting Point80-100°C
Popular Categories in Dezhou