Polyurethane Sealant - Polyurethane, Black, 1.2kg/l, Moisture Cure, Anti-sag | Strong Bond, Durable Seal, 30 Min Cure, <1% Shrinkage, 6 N/mm2 Tensile Strength

Polyurethane sealant

Chemical based polyurethane

Anti sag is very good, do not sag

Density (006-4 CQP) about 1.2kg/l

Curing mechanism moisture curing

Color (001-1 CQP1) black

Shrinkage rate (014-1 CQP) <1%

Curing rate (049-1 CQP) with reference to figure 1

Construction time 2 (526-1 CQP) about 30 minutes

Table dry time 2 (019-1 CQP) about 45 minutes

Construction temperature of + 10 DEG C DEG C to 35

G modulus (081-1 CQP) 0.7N/mm2

Shear strength (046-1 CQP / ISO 4587) was about 4.5N/mm2

Tear strength (045-1 CQP / ISO 34) was about 10 N/mm

Fracture elongation (036-1 CQP / ISO 37) 450%

Tensile strength (036-1 CQP / ISO 37) was about 6N/mm2

Shao A hardness (023-1 CQP / ISO 868) was about 45

Working temperature (CQP 513-1) long of-40 DEG C DEG C to 90

Resistance coefficient (079-2 CQP / D 257-99 ASTM) about 106 Wcm

The glass transition temperature (CQP 509-1 / ISO 4663) about 45 DEG C

G modulus (081-1 CQP) 0.7N/mm2

BottledShelf life (25 degree C the following seal preservation) (016-1 CQP) hard and soft support 6 months/9 months