Yttria Stabilized Zirconia Beads By Far Ocean Zirconia Co.,ltd

Yttria Stabilized Zirconia Beads are manufactured from dry Yttria Stabilized Zirconia powder by high compaction press. They was sintered at a high temperature to form a Tetragonal Zirconia Polycrystal(Y-TZP) microstructure. The highest bending strenghth and fracture toughness was considered the first choice of grinding media to mill the most sensitive powder or slurry.

Advantage:
1.Preventing material from contamination because of its extreme low wear rate.
2.High grinding efficiency.
3.Lower total costs due to the long using life.

Usage:
Materials for grinding and dispersed, Structural Ceramics,Electronics Ceramics, Refractory Ceramics, Magnetic material, Metallurgy, medicine,food, cosmetics, paints, textiles, printing and dyeing, pigment and other industries.

Sizes:
Sphere: 1,1.5,2,2.5,3,5,7,10a 55mm
Cylinder 3A 3,5A 5,7A 7,10A 10,12A 12mm

Wear resistance compared with the other grinding media:
CompositionWt%95%Zro2, 5%Y2O3
Specific densityG / cm3a Y5.95
Hardness (HV))HRA10
Thermal expansion Coefficient(20~400) (10-6/k) 11
Elastic modulisGpa205
Fracyure toughnessMpa . m 1/27-10
Bending strengthMpa1150
Grain sizeI m0.5
Thermal conductivityW / (m.k)3

Criteria in Selecting Size of Zirconia Grinding Media
1.Larger-sized media are more efficient in breaking up large particles.
2.Smaller media are more efficient in milling smaller particles because of higher effective contact area.
3.Larger media sizes are favored in many conventional ball mills. Smaller sizes are more appropriate for attritors. For example, 5mm media are used in many attrition mill applications, whereas 10-15 mm may be a good start for a lab ball mill. For small-media mills, media sizes are typically smaller than 2 mm.
4 Another important criterion in selecting media size is the gap size between stirring arms and mill walls. Media size should be significantly smaller than the gap size to prevent jamming.